International Tables for Crystallography (2010). Vol. B, ch. 2.5, p. 352   | 1 | 2 |

Figure 2.5.3.24 

M. Tanakaf
[Figure 2.5.3.24]
Figure 2.5.3.24

Three pairs of ZOLZ [(a), (c) and (e)] and HOLZ [(b), (d) and (f)] CBED patterns taken at 60 kV from an area of Al74Mn20Si6 about 3 nm in diameter and about 10 nm thick (Tanaka, Terauchi, Suzuki et al., 1987[link]). Symmetries are (a) 10mm, (b) 5m, (c) 6mm, (d) 3m, (e) 2mm and (f) 2mm.