International
Tables for
Crystallography
Volume D
Physical properties of crystals
Edited by A. Authier

International Tables for Crystallography (2013). Vol. D, ch. 3.4, p. 527

Table 3.4.3.7 

V. Janoveca* and J. Přívratskáb

aInstitute of Physics, Academy of Sciences of the Czech Republic, Na Slovance 2, CZ-18221 Prague 8, Czech Republic, and bDepartment of Mathematics and Didactics of Mathematics, Technical University of Liberec, Hálkova 6, 461 17 Liberec 1, Czech Republic
Correspondence e-mail:  janovec@fzu.cz

Table 3.4.3.7| top | pdf |
Ferroelastic domain pairs with no compatible domain walls

[F_1] is the symmetry of [{\bf S}_1], [g_{1j} ] is the switching operation, [K_{1j}] is the twinning group. Pair is the domain pair type, where ns is non-transposable simple and nm is non-transposable multiple (see Table 3.4.3.2[link]). [ v= z], [p=[111]], [q=[\bar 1\bar 11]], [r =[1\bar 1\bar 1]], [s=[\bar 1 1 \bar 1]] (see Table 3.4.2.5[link] and Fig. 3.4.2.3[link]).

[F_1][g_{1j} ][K_{1j} ]Pair
[1 ] [4_z ] [4_z ] ns
[1 ] [\bar4_z] [\bar4_z ] ns
[1 ] [3_v] [3_v] ns
[1 ] [\bar3_v] [\bar3_v] ns
[1 ] [6_z ] [6_z ] ns
[1 ] [\bar6_z] [\bar6_z ] ns
[\bar1 ] [4_z], [4_z^3] [4_z/m_z ] ns
[\bar1 ] [3_v], [3_v^2] [\bar3_v] ns
[\bar1 ] [6_z], [6_z^5] [6_z/m_z ] ns
[2_z ] [3_p], [3_p^2] [2_z3_p ] nm
[2_z ] [\bar3_p], [\bar3_p^5 ] [m_z\bar3_p] nm
[2_{xy} ] [3_p], [3_p^2] [4_z3_p2_{xy} ] nm
[2_{xy} ] [\bar3_p], [\bar3_p^5 ] [m_z\bar3_pm_{xy}] nm
[m_z ] [3_p], [3_p^2] [m_z3_p^2 ] nm
[m_{xy} ] [3_p], [3_p^2] [\bar4_z3_pm_{xy} ] nm
[m_{xy} ] [4_x], [4_x^3] [m_z\bar3_pm_{xy}] nm
[2_z/m_z ] [3_p], [3_p^2] [m_z\bar3_p] nm
[2_{xy}/m_{xy} ] [3_p], [3_p^2] [m_z\bar3_pm_{xy}] nm
[2_x2_y2_z ] [3_p], [3_p^2] [2_z3_p ] ns
[2_x2_y2_z ] [\bar3_p], [\bar3_p^5 ] [m_z\bar3_p ] ns
[m_xm_y2_z ] [3_p], [3_p^2 ] [m_z\bar3_p ] nm
[m_xm_ym_z ] [3_p], [3_p^2 ] [m_z\bar3_p ] ns