Table 2.3.2 

C. J. Howarda* and E. H. Kisia

aSchool of Engineering, University of Newcastle, Callaghan, NSW 2308, Australia
Correspondence e-mail:  chris.howard@newcastle.edu.au

Table 2.3.2| top | pdf |
Coherent scattering lengths and absorption cross sections (for 25 meV neutrons) for selected isotopes

Data are taken from Section 4.4.4[link] of Volume C (Sears, 2006[link]). Where not stated, the values are for the natural isotopic mix. The X-ray atomic form factors, f, evaluated at Q = 1.2π Å−1, are included for comparison.

ElementIsotopebcoh (fm)σs(tot) (10−24cm2)σa (10−24cm2)fIsotopic abundance (%)
H   −3.7390 (11) 82.02 (6) 0.3326 (7) 0.25  
  1 −3.7406 (11) 82.03 (6) 0.3326 (7)   99.985
  2 6.671 (4) 7.64 (3) 0.000519 (7)   0.015
  3 4.792 (27) 3.03 (5) 0  
             
B   5.30 (4) − 0.213 (2)i 5.24 (11) 767 (8) 1.99  
  10 −0.1 (3) − 1.066 (3)i 3.1 (4) 3835 (9)   20.0
  11 6.65 (4) 5.78 (9) 0.0055 (33)   80.0
             
C   6.6460 (12) 5.551 (3) 0.00350 (7) 2.50  
  12 6.6511 (16) 5.559 (3) 0.00353 (7)   98.90
  13 6.19 (9) 4.84 (14) 0.00137 (4)   1.10
             
O   5.803 (4) 4.232 (6) 0.00019 (2) 4.09  
             
Ti   −3.370 (13) 4.06 (3) 6.43 (6) 13.2  
  46 4.725 (5) 2.80 (6) 0.59 (18)   8.2
  47 3.53 (7) 3.1 (2) 1.7 (2)   7.4
  48 −5.86 (2) 4.32 (3) 8.30 (9)   73.8
  49 0.98 (5) 3.4 (3) 2.2 (3)   5.4
  50 5.88 (10) 4.34 (15) 0.179 (3)   5.2
             
V   −0.3824 (12) 5.10 (6) 5.08 (2) 14.0  
             
Ni   10.3 (1) 18.5 (3) 4.49 (16) 18.7  
  58 14.4 (1) 26.1 (4) 4.6 (3)   68.27
  60 2.8 (1) 0.99 (7) 2.9 (2)   26.10
  61 7.60 (6) 9.2 (3) 2.5 (8)   1.13
  62 −8.7 (2) 9.5 (4) 14.5 (3)   3.59
  64 −0.37 (7) 0.017 (7) 1.52 (3)   0.91
             
Cu   7.718 (4) 8.03 (3) 3.78 (2) 19.9  
  63 6.43 (15) 5.2 (2) 4.50 (2)   69.17
  65 10.61 (19) 14.5 (5) 2.17 (3)   30.83
             
Zn   5.680 (5) 4.131 (10) 1.11 (2) 20.8  
             
Zr   7.16 (3) 6.46 (14) 0.185 (3) 27.0  
             
Gd   6.5 (5) 180 (2) 49700 (125) 45.9  
  155 6.0 (1) − 17.0 (1)i 66 (6) 61100 (400)   14.8
  157 −1.14 (2) − 71.9 (2)i 1044 (8) 259000 (700)   15.7
             
Pb   9.405 (3) 11.118 (7) 0.171 (2) 60.9