International
Tables for
Crystallography
Volume H
Powder diffraction
Edited by C. J. Gilmore, J. A. Kaduk and H. Schenk

International Tables for Crystallography (2018). Vol. H, ch. 2.8, p. 181

Figure 2.8.10 

H. Ehrenberg,a* M. Hinterstein,a A. Senyshynb and H. Fuessc

aInstitut für Angewandte Materialien (IAM-ESS), Karlsruhe Institut für Technologie (KIT), Eggenstein-Leopoldshafen, Germany,bTechnische Universität München, Garching b. München, Germany, and cTechnische Universität Darmstadt, Darmstadt, Germany
Correspondence e-mail:  helmut.ehrenberg@kit.edu

[Figure 2.8.10]
Figure 2.8.10

The pseudo-cubic 002 reflection of (a) 0.93BNT–0.07BT end member, (b) 0.938BNT–0.053BT–0.009KNN, (c) 0.932BNT–0.045BT–0.023KNN and (d) 0.86BNT–0.14KNN end member as a function of electric field from the initial zero-field state (top) to an applied field of 5.5 kV mm−1 (bottom). The sample orientation is such that the scattering vector is parallel to the electric field. Reproduced with permission from Daniels et al. (2010[link]). Copyright (2010) Elsevier.